MCA White Flame Retardant Masterbatch (FR-MCA500)

Click on the image to check the artwork
unit price: negotiable
min amount:
amount:
period for delivery: Consignment Deadline Days
area: Beijing
Expiry date : Long Effective
last update: 2017-12-21 08:03
view count: 366
enquiry
Company Profile
 
 
Product details

Introduction

FR-MCA500 using PA6 resin as carrier, content of MCA is above 50%, Advantages: good compatibility with PA6 and PA66 resin, good dispersity, good flame resistance. Environmental protection without halogen, low dosage, no mold corrosion, high effective, low smoke, high cost performance. Flame retardant can reach the level UL94V0.

Index

Item

FRMCA500

FRMCA500H

Appearance

White Granular

Black Granular

Content wt%

50

50

Carrier

PA6

PA6

Density g/cm3

1.2±0.2

1.2±0.2

Solubility Index g/min

230

230

Decomposition Temp ℃

320

320

Water Content wt%

≤0.3

≤0.3

Note

1.FR-MCA500 is suitable for various processing temperature of black nylon 6 and nylon 66, non-discolouring, excellent mechanical properties. Don't catch fire with CTI 600℃, glowing filament 750℃.

2.Suggest adding raw material nylon and drying at 120 ℃ to 4-6 hours; processing temperature is 230-250℃.

3.If you have more detailed requirements for your products, we can provide different design solutions according to your requirements, In order to bring you more convenience and save more cost.

Performance and Advantage

MCA500 mainly used in products which with high flame retardant requirement. Such as, PA bellow, PA conduit, thin-wall products etc., injection and extrusion.

Item

PA66 Resin

FR-MCA500

FR-MCA500H

Add 15%

Add 15%



Tensile Strength MPa

≥70

≥60

≥60

Izod Impact Strength Notched KJ/m2

≥10

≥9

≥9

Tensile Strength MPa

≥100

≥100

≥100

Density g/cm3

1.10-1.15

1.2

1.2

Melting Temp ℃

238-248

245-250

245-250

Flame Retardancy UL94 3.2/1.6mm

Non flame retardant

V0

V0

Characteristic


High brightness,No crystal point

Black, high level flame retardant

Packing/Storage

25KG/bag: paper-plastic composite plus polyethylene lining plastic bag packaging, stored in dry and cool place, avoid direct sunlight.



Total0bar [View All]  Related Comments
 
More>other products

[ ProductsSearch ]  [ Send Fav ]  [ Share ]  [ Print ]  [ Send Report ]  [ Close ]

 
Home | Products | Suppliers | News | Tradeshow | Sitemap | Message | RSS Feed